Scrapchap: Asking for a few tips on Toroidal Transformers
Evening scrappers!
It took me roughly 15-20min to melt it out, and another hour and a half to remove primary and secondary windings. The smaller windings look like a some kind of aluminum wire with a red varnish to make it look like copper.
The other problem I am having is that when I remove the larger copper wire, have all this tar like or plastic material all over it.
I appreciate the help y'all!
Happy Scrapping!
I would not burn them at all. If you can't whack it with a hammer or similar i suggest you sell them as motors (a.k.a. copper bearing material, CBM). Most all electronics and electrical material is better off not burned because it can and does release dangerous chemicals. Mike.
"Profit begins when you buy NOT when you sell." {quote passed down to me from a wise man}
Now go beat the copper out of something, Miked
Metal Recycling Entrepreneur
Well these transformers are inside of a underwater light. The transformer is coated in this thick plastic. I tried chiseling but it took incredibly too long to even chip the surface to see the windings. Is there a chemical solution I can use to loosen the transformer possibly clean all this harden plastic?
|
What ever you use is going to cost more than what you recoup in copper price, just hope your yard accepts burnt copper. Some don't.Originally Posted by scrapchap
P & M Recycling - Specializing in E-Waste Recycling.
If you enjoy your freedom, thank a vet.
That there looks like an exercise in futility. I know, I've been there.
Yes take the advise and spend your time more productively on other things. Like you I would tear open everything I could, like you I learned that many things just aren't worth breaking down. Mike
Metal Recycling Entrepreneur
Burn it hotter, longer.
|
If it is old it could contain PCBs.
"anyone who thinks scrappin is easy money ain't doin it right!"
Metal Recycling Entrepreneur
Nah I checked it is just Iron core with primary and secondary copper windings. The smaller windings were this reddish copper, but after scratching the wire it was not copper. Some kind of varnish or coating on aluminum wire I think.
Metal Recycling Entrepreneur
|
If the wire isn't copper, why would you break it down. Seems like a waste of time even if it is copper. I'm with the other guys, spend your time with a more profitable break down.
-
Scrapchap: Need some scrappers knowledgeThere are currently 2 users browsing this thread. (0 members and 2 guests)
|
Browse the Most Recent Threads
On SMF In THIS CATEGORY. 
OR 
|
Posting Permissions
Register To Reply
Bookmarks